Beth yw'r Crynodiad Silica Uchaf a Ganiateir (ppm) mewn Datrysiad Sodiwm Hydrocsid 25% ar 90 gradd i Atal Ffurfio Graddfa Sodiwm Titanad Sy'n Inswleiddio Tiwb Gwresogydd Titaniwm Gradd 2?

Silica (SiO2) interacts with titanium in 25% sodium hydroxide at 90°C to create sodium titanate (Na2TiO3) and sodium silicate scale. These scales have a relatively low thermal conductivity (0.5–1.5 W/m·K). Silica The maximum concentration of silica allowed to prevent the formation of insulating scale is 50 ppm. A scale thickness of >0.1 mm in 500 hours at >Cynhyrchir 50 ppm, gan arwain at golled sylweddol o drosglwyddo gwres.

Crynodiad Silica vs Ffurfiant Graddfa Feintiol

90 gradd am 500 awr mewn 25% NaOH:

Silica (ppm) Trwch Graddfa (µm) Graddfa Cyfansoddiad Lleihau Trosglwyddiad Gwres (%)
0 0 Dim 0 10 5–15 Sodiwm silicad 2–5 25 15–40 Silicad/titanad cymysg 5–15 50 40–80 Titanad sodiwm sy'n dominyddu 15–30 100 80–150 Titanad trwchus 30–50 250 150–300 Effaith goddefiant silicad ar raddfa drom 5–15 50 40–80

Tymheredd ( gradd ) Max Silica ar gyfer<0.1 mm Scale (ppm)Recommended Max (ppm) Silica Control Guide 70 100 75 80 75 50 90 50 30 100 30 20

Silica wedi'i Fesur (ppm) Cam Gweithredu a Argymhellir Graddfa Ddisgwyliedig Trwch (micronau/blwyddyn)
<20 No <20
20–50 Monitor Monthly 20-80 50-100Dilute or filter solution 80-150 >100 Replace solution >150
Argymhelliad ar gyfer Peirianneg

Ar gyfer 25% NaOH ar 90 gradd, dylid cadw'r crynodiad silica o dan 30 ppm. Er mwyn atal halogiad silica, defnyddiwch ddŵr wedi'i ddad-ïoneiddio i'w wanhau. Mae'r peiriannydd yn rheoli'r silica i atal creu graddfa titanate sodiwm inswleiddio.